Dry Offset Printing Blankets from China manufacturer

Consumables

Home Consumables Rubber Blankets Dry Offset Printing Blankets

Dry Offset Printing Blankets

Designed for dry offset printing on two-piece can decorators. The self-adhesive construction ensures secure mounting, easy installation and reliable performance throughout long production runs.

Printing Process
Dry Offset Printing

Suitable Equipment
Two-piece Can Decorators

Mounting Type
Self-Adhesive

Available Color
Blue

库存： 0

Inquire Now

Product Overview

Printing Characteristics

Main Application

Technical Specification

Material Structure

Product Overview

Formed from a single piece of metal (usually aluminum or tinplate) using a deep drawing process to create the body and bottom as one piece, then adding the end. Printing is done before forming.

Optimized for Pre-Forming Printing

Specifically designed for printing on flat aluminum or tinplate sheets before the deep drawing process forms the can body and bottom as one integrated piece.

High-Strength Metal Reinforcement

Multi-layer construction ensures excellent dimensional stability, preventing stretching or distortion during high-speed metal decorating.

Precision Compressible Layer

Engineered compressible layer provides uniform pressure distribution, ensuring consistent ink transfer prior to forming and maintaining image integrity after deep drawing.

Abrasion-Resistant Surface Compound

Durable elastomer surface withstands continuous contact with metal sheets, reducing wear and extending service life in demanding can-printing environments.

Printing Characteristics

High-performance compressible rubber blanket with blue surface

Designed for metal decorating / two-piece can printing

Offers stable pressure control, good resilience and long service life under

High-load printing conditions

Main Application

Technical Specification

Item	Value
Type	Compressible
Colour	Blue
Construction	3 piles
Thickness	1.96 mm
Thickness tolerance	±0.02 mm
Hardness	78°Shore A
Surface Roughness (Ra)	1 µm
Compressibility at 100 N/cm²	0.15 mm (≈ 7.65% thickness change)
Durability test	≤3% gauge loss
Loss of compressibility after fatigue test	≤40% loss of compressibility
Flexibility	30° (no cracking at bending test)
Tensile Strength	92 N/mm
2% Modulus	64 N/mm
Elongation at break	3.1%
Stickiness	6 N/25 mm

Material Structure